Fiber Surface Modification; Characterization of Rattan Fiber Reinforced Composite, International Journal of Engineering & Technology, 7 (3.7) (2018) 113-116, TURNITIN RESULT

Firdaus, Flora Elvistia (2018) Fiber Surface Modification; Characterization of Rattan Fiber Reinforced Composite, International Journal of Engineering & Technology, 7 (3.7) (2018) 113-116, TURNITIN RESULT. Science Publishing Corporation.

[img] Text
13. Turnitin - J_Fiber_Surface_Modification_Characterization_of_Rat_Scipub_J_5.pdf

Download (1MB)

Abstract

Increasing the awareness of global warming and the depletion of petroleum resources had made many researchers focuses on using natu-ral materials such as rattan. Its an edible fibers are prepared to reinforce matrix yielding composite products within the aid of epoxy based resin and hardener which also perform as catalyst. The fibres are previously conducted an alkali treatment, this was considered to enhance the cohessiveness of fibers to matrix. Silane and dimethylethanolamine (DMEA) as an adhesives booster is respectively added to the composite formula. The specific purpose of this research is to know the influence of addition of Silane and DMEA to the final properties of composite; flexural, tensile strength, elongation at break, hardness, and thermal. From the test results it is found that Silane keeps the matrix amorphous, while the addition of DMEA formed crystalline polymer. The ultimate property of the composites are found also depends on fiber woven pattern.

Item Type: Other
Subjects: T Technology > TA Engineering (General). Civil engineering (General)
Depositing User: Dr FLORA ELVISTIA FIRDAUS
Date Deposited: 01 Dec 2021 06:16
Last Modified: 01 Dec 2021 06:16
URI: http://repo.jayabaya.ac.id/id/eprint/1366

Actions (login required)

View Item View Item